Sound-record tablet. Download PDFInfo
- Publication number
- US1207383A US1207383A US74523213A US1913745232A US1207383A US 1207383 A US1207383 A US 1207383A US 74523213 A US74523213 A US 74523213A US 1913745232 A US1913745232 A US 1913745232A US 1207383 A US1207383 A US 1207383A
- Authority
- US
- United States
- Prior art keywords
- binder
- weight
- filler
- veneer
- tablet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
T. A. EDISON.
SOUND RECORD TABLET.
APPLYICATION FILED JAN. 30. 1913.
1 .QYfi Patented Dec. 5, 1916.
PHEHOLIC FIHRL COHDEHSHTION PRODUCT VLH5TIC fiT ELEVBTED TEMPERHTURES VIIIIIII'IIIIIIIIIIIIIII IIIIII -11. IIIIIIIIIIIIIII IIIII ONE PfiRT THERIYIUPLRSTIC BINDER T0 HT LEHST 33'; PARTS OF FIBROUS FILLER if It l l U a THOMAS A. EDISON, OF LLEWELLYN PARK, WEST ORANGE, NEW JERSEY, ASSIGNOR TO NEW JERSEY PATENT COMPANY, WEST ORANGE, NEW JERSEY, A CORPORATION OF NEW JERSEY.
Specification of Letters Patent.
SOUND-RECORD TABLET.
Application filed January 30, 1913. Serial No. 745,232.
T 0 all whom it may concern:
Be it known that I, THOMAS A. EDISON, a citizen of the United States, and a resident of Llewellyn Park, West Orange, in the county of Essex and State of New Jersey, have invented certain new and useful Improvements in Sound-Record Tablets, of which the following is a description.
My invention relates to sound record tablets and more particularly, but not eXclu sively, to composite disk shaped sound record tablets having a body containing a fibrous inert filler and a surface veneer of a material adapted to receive a sound record impression. Both the body and the surface veneer in the preferred tablet-s contemplated by this invention are thermo plastic, that is, they are adapted to be rendered plastic by the application of heat, the body being preferably fusible or thermo plastic to a larger degree than the surface veneer. The preferred composition for the body of the tablet is composed of a filler, such as wood flour, together with a binder of fusible resin, such as the phenol or cresol resin formed by reaction between definite amounts of phenol or cresol and formaldehyde or equivalents. The resin I preferably employ melts at approximately 2:20 Fahr. and when subjected topressure in the mold with the application of sufficient heat flows between the mold plates so as to permit an even printing of the record tablet. The surface veneer is preferably formed of a hard final phenolic condensation product, such-as described in U. S. Patents to Jonas W. Aylsworth, Nos. 1,020,593, 1,046,137 and 1,046,420, this composition containing a plasticity ingredient, such as penta-chloro-phenol, whereby upon application of sufiicient heat the surface veneer may be rendered suliicien'tly plastic to receive a sound record impression. I prefer to use for the veneer a composition of this last named class which becomes plastic at about 320 Fahr. When a tablet having a veneer and body of the preferred compositions mentioned above is subjected in the mold to the necessary temperature and pressure to impress the sound waves in the surface of the veneer, the body, because of the fluid condition of the binder, will have a tendency to flatten out. this tendency being resisted by the fibrous filler.
The principal object of my invention is to provide a sound record tablet of the class described which can be repressed to eliace an old record impression and to form a new record impression in the surface of the tablet a number of times Without objectionable increase in diameter, decrease in thickness, or other objectionable change in shape.
Another object of my invention is to provide a sound record tablet provided with a surface veneer having such hardness, thickness, or other characteristics that the rough filler of the backing cannot be impressed into the outer surface of said veneer during the repeated repressing of the tablet.
Other objects of my invention will appear more fully in the following specification and appended claims.
In order to prevent objectionable change in shape in the tablet during the repressingthereof, I find that the proportion of the fibrous filler with respect to the binder in the body of the tablet must not be less than a given amount. lVhen the proportion of the filler to the binder is less than this amount,
as has heretofore been the case, the lateral flow of the composition forming the body of the tablet each time the tablet is reheated and repressed produces an objectionable enlargement of the diameter of the tablet and a corresponding reduction in the thickness thereof; so that there is such a variation between the shapes of the new records which have been pressed and molded only once and the records which have been repressed anumber of times that the uniformity of shape and size desired for a commercial record is not obtained. The relative amounts of filler and binder which are necessary depend, of course, to some extent, upon the materials employed for the filler and binder. When the binder is formed of the fusible resinous condensation products referred to above or other similar products, and the filler is formed of wood flour, I find that the Weight of the Wood flour should not be less than three and a half times the weight of the resin. The preferred proportion by weight of the fibrous filler to the resinous binder referred to is four to one, but this proportion may be increased up to four and onehalf or even five to one. A. tablet having a body formed of these proportions of fusible binder and fibrous filler may be readily repressed or reprinted at least ten times without undergoing any objectionable increase in diameter and decrease in thickness.
The thickness of the surface veneer to prevent the fibers in the body of the record from being pressed through the veneer to the outer surface thereof during the pressing or re-pressing of the record depends upon the composition of which the veneer is formed. When the veneer is formed of the thermo plastic hard final phenolic condensation products referred to, the thickness thereof should be not less than .0015 of an inch and should preferably be about .0025
' of an inch.
In the preferred form of my invention, the title of the record and the sound record impression are impressed into the surface of the tablet at the same time, as shown, for example, in an application of Jonas W. Aylsworth and Edward L. Aiken, Serial No. 704,517, filed June 17, 1912, and entitled improvements in the production of sound records. Obviously, when the title is impressed lnto the record tablet in this way, a single operation is sufficient to eiiace the old record impression and title and to imprint in place thereof the new record impression and title.
Various compositions other than those .mentioned above may be used for forming the veneer and the body of the record. Thus the veneer may be formed of celluloid and the binder may be formed of copal gum, shellac or numerous other resinous composi tions.
The invention in some of its aspects is not limited to a record tablet having a separate veneer secured to a suitable body.
In the drawing forming a part of this specification is shown a cross section of one embodiment of my invention, the material employed in the said embodiment being de' scribed in the drawing.
What I claim as new and desire to protect by Letters Patent of the United States is as follows:
1. As a new article of manufacture, a sound record tablet having a body composed of a thermo-plastic binder and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight offiller, and a surface veneer for said body composed of a final phenolic condensation product which is sufiiciently plastie at elevated temperatures to be molded, substantially as described.
2. As a new article of manufacture, a sound record tablet having a body composed of a binder of thermo-plastic condensation product and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product which is sufiiciently plastic at elevated temperatures to be molded, substantiially as described.
3. As a new article of manufacture, a sound record tablet having a body composed of a thermo-plastic phenolic binder and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product which is sufficiently plastic at elevated temperatures to be molded, substantially as described.
4. As a new article of manufacture, a sound record tablet having a body composed of a thermoplastic binder of condensation product and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, substantially as described.
As a new article of manufacture, a sound record tablet having a body composed of a thermoplastic phenolic binder and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, substantially as described.
6. As a new article of manufacture, a sound record tablet having a body composed of a thermo-plastic binder and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product which is sufiiciently plastic at elevated temperatures to be molded, said veneer being at least .0015 of an inch in thickness, substantially as described.
7. As a new article of manufacture, a sound record tablet having a body composed of a thermo-plastic binder and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product which is sufiiciently plastic at elevated temperatures to be molded, said veneer being approximately .0025 of an inch in thickness, substantially as described.
8. As a new article :ofmanufacture, a disk shaped sound record tablet having a body composed of a fusible binder and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product containing a plasticity ingredients, substantially as described.
9. As a new article of manufacture, a sound record disk having a body composed of a fusible binder and a finely divided fibrous filler in the proportion of one part by weight of binder to four parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product containing a plasticity ingredient, substantially as described.
, 10. As a new article of manufacture, a disk shaped sound record tablet having a body composed of a binder of fusible resin and a fibrous filler in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product containing a plasticity ingredient, substantially as described;
11. As a new article of manufacture, a disk shaped sound record tablet having a body composed of a fusible binder and filler of wood flour in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a surface veneer for said body composed of a final phenolic condensation product containing a plasticity ingredient, substantially as described.
12. As a new article of manufacture, a disk shaped sound record tablet .having a body composed of a binder of fusible resin and filler of wood flour in the proportion of one part by weight of binder to at least three and a half parts by Weight of filler, and a surface veneer for said body composed of a final phenolic condensation product containing a plasticity ingredient, substantially as described.
13. As a new article of manufacture, a sound record tablet having a body composed of a fibrous filler and a fusible binder in the proportion of one part by weight of binder to at least. three and a half parts by weight of filler, and a thermo plastic Veneer on said body, the temperature at which said binder melts being lower than that at which said veneer becomes plastic substantially as described.
14. As a new article of manufacture, a sound record tablet having a body composed of a fibrous filler and a binder which melts at a temperature less than 300 degrees Fahr. in the proportion of one part by weight of binder to at least three and one-half parts by weight of filler, and a veneer for said grees Fahr. in the proportion of one part by weight of binder to at least three and one-half parts by weight of filler, and a veneer for said body which becomes plastic at a temperature of approximately 320 degrees Fahn, substantially as described.
16. As a new article of manufacture, a sound record tablet having a body composed of a finely divided fibrous filler and a fusible binder in the proportion of one part by weight of binder to at least three and a half parts by weight of filler, and a thermo plastic veneer on said body, the temperature at which said binder melts being lower than that at which said veneer becomes plastic, substantially as described.
17. Asa new article of manufacture, a sound record tablet having a body composed of a finely divided fibrous filler and a binder which melts at a temperature less than 300 degrees Fahr. in the proportion of one part. by weight of binder to at least three and one-half parts by weight of filler, and a veneer for said body which becomes plastic at a temperature above 300 degrees Fahra, substantially as described.
18. As a new article of manufacture, a sound record tablet having a body composed of a finely divided fibrous filler and a binder which melts at a temperature of approximately 220 degrees Fahr. in the proportion of one part by weight of binder to at least three and one-half parts by weight of filler, and a veneer for said body whichbecomes plastic at a temperature of approximately 320 degrees Fahr.,substantially as described.
This specification signed and witnessed this 29th day of January, 1913.
THOS. A. EDISON.
Witnesses: Y
FREDERICK BACHMANN, MARY J. LAIDLA Correction in Letters Patent No. 1,207,383.
It is hereby certified that in Letters Patent N o. 1,207 383, granted Deceinber 5, 1916, upon the application of Thomas A. Edison, oi Llewellyn Park, West Orange, New Jersey, for an improvement in Sound-Record Tablets, an error appears in the printed specification requiring correction as follows: Page 2, line 124,, claim 8, for the word .ing -redients read ingredient; that the said Letters Patent should be read with this correetion therein that the same may conformto' the record of the case in the Patent Oifice.
Signed and sealed this 13th day of February, A. D., 1917 [SEAL] R. F. WHITEHEAD,
\ Acting Commissioner of Patents. 01. 164 43.