Images

Classifications

• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
  • H01M4/00—Electrodes
  • H01M4/02—Electrodes composed of, or comprising, active material
  • H01M4/04—Processes of manufacture in general
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
  • Y02E60/10—Energy storage using batteries

Definitions

• My invention relates to storage battery electrode elements and more particularly to electrode elements designed for use in storage battery cells having the same general characteristics as the cell disclosed in Patent No. 1,377,194: granted to me on May 10, 1921, and to the production of such elements.
• electrode elements in accordance with my invention are designed especially for use in connection with Edison storage battery cells, wherein nickel hydroxide is opposed to finely divided electrolytically active iron or oxide of iron in an alkaline solution as the electrolyte, it is to be distinctly understood that my invention is not limited in its application to cells of this type.
• a battery pile of special construction is employed in the place of the usual plate assembly in Edison storage battery cells.
• This battery pile comprises a series of very thin conductive contact sheets, preferably of nickel, separated by insulating sheets preferably of asbestos paper, with thin flat layers of finely divided active material respectively disposed between the surfaces of each of the nickel sheets and the adjacent asbestos sheets, the whole being held together under great pressure with the layers of active mate rial in firm close surface contact with the respective nickel sheets.
• the layers of active material for the negative elements preferably consist of electrolytically active finely divided iron or oxide of iron, preferably mixed with a small amount of mercury, and
• the layers of active material for the positive elements preferably consist of finely divided nickel hydroxide.
• suitable active materials may however, be employed instead of the finely divided iron and nickel hydroxide; for example, in place of finely divided iron as the active material for the negative elements, finely divided cadmium or cobalt maybe employed; and in place of nickel hydroxide as the active material for the positiveelements, an oxide of cobalt may be employed.
• the insulating sheets, preferably of asbestos, used in the battery pile were first coated by a wet rocess on one side with a thin layer of nely divided iron or oxide of iron, and on Ill) the other side with a thin la er of nickel hydroxide. These coated as estos sheets were then partially dried and subjected to enormous pressure, for example a pressure of several tons per square inch, so as to compact the layers of active material and form the same with very smooth flat surfaces.
• the surface contact of the nickel conductive sheets and the layers of active material engaging the same is so close and said layers of active material ? 1m so compacted because of the great pressure to which said layers were subjected 1n forming the battery pile, and also because of the pressure under which the pile is maintained, that it is extremely difficult for any appreciable amount of the electrolyte to gain access to the layers of active material except such portions thereof as are directly exposed to or closely adjacent the body of the electrolyte in the cell.
• the internal resistance and heating ofsuch a cell both on charge and discharge are materially increased by osmotic action.
• This action takes place in the direction of the flow of current and when the cell is on charge has the effect of driving the small amount of electrolyte which might otherwise reach those portions of the layers of active material of the positive electrode elements which are remote from the body of the electrolyte, away from the adjacent surface portions of the conductive contact sheets of such elements; while when the cell is discharged it has theeifect of driving the electrolyte which might other wise reach the corresponding portions of the layers of active material of the negative elements, away from the adjacent surface portions of the conductive contact sheets of these elements.
• the adjacent active material is rendered practically dry arid as such material is a very poor conductor when dry, the electrical resistance thereof and the internal resistance of the cell will thereupon be greatly increased.
• My invention is especially directed to the production of electrode elements comprising coated sheets of asbestos or other suitable insulating material which are in general, similar to the coated asbestos insulating sheets produced in carrying out the process above described, and resides in an improved form of electrode element of this character whereby in cells comprising battery piles made up of such elements, the circulation of the electrolyte will be so improved and increased as to insure a constant and copious supply of electrolyte to all portions of the various layers of active materials of the electrode elements both on charge and discharge.
• My invention also resides in an improved process or method of producing such coated insulating sheets and in improved apparatus adapted for carrying out such process.
• My co-pending application Serial No. 225,619, filed October 12, 1927, is a division hereof and contains claims covering my improved apparatus.
• My improved process is essentially a dry process and I have discovered that coated insulating sheets such as those referred to, may be produced much more economically by such process than by the wet rocess heretofore used.
• Briefiyaglescribe such improved process consists in applying to one or each side of a support preferably a sheet of fibrous insulating material such as asbestos, a thin and preferably channeled layer of finely divided'active material in a dry loose state free from a binder, the layer or la ers of active material being applied to the s wet in such a way as to be of substantially uniform thickness.
• the asbestos sheet with the channeled layer or layers of active material applied thereto is then subjected, as by means of a hydraulic press, to a very heavy pres sure, for example, a pressure of from 2 to 10 tons per square inch.
• a very heavy pres sure for example, a pressure of from 2 to 10 tons per square inch.
• each layer of dry finely divided oose active material is firmly united to the insulating sheet and is agglomerated and compacted into a dense coherent but channeled sheet or layer of such material of substantially uniform thickness, this layer being formed wholly of active material and bein free from any binder.
• one layer consists of active material for the negative electrode elements, prefrably iron or oxide of iron, and the other layer consists of active material for the ositive electrode element, preferably nickel hydroxide.
• Figure 1 is a plan view of one form of my improved apparatus for applying layers of finely divided dry active material to insulating sheets or other supports, in accordance with my improved rocess;
• Figure 2 is a view in side e evation, partly in section, of the apparatus shown in Figure 1;
• FIG. 3 is a plan view of an electrode element in accordance with my invention.
• Figure 4 is a sectional view on line 44 of Figure 3;
• Figure 5 is a view similar to Figure 4, showing an insulating sheet having a channeled layer of active material applied to but one side or surface thereof:
• the channel 4 extends the whole length of the base 1 and is provided at its opposite sides with guiding grooves 5.
• the base 1 has a large rectangular opening A extending therethrough, said opening comprising a-lowersection 6 of the same shape and size opening, are
• the opening A is provided with flanges 8 on all four sides, which flanges define the section 7 of the flush with the bottomof the channel 4 and have a thickness corresponding to the desired thickness of the layers of active material applied to the insulating sheets before subjecting the same to pressure. At a small distance beyond one end of opening A.
• the bottom of the channel 4 of base 1 is also provided with an inclined opening 9 extending therethrough and transversely thereof, the said opening 9 providing for the discharge of the surplus active material deposited from the hopper 3 of the apparatus in applying a layer of such material to an insulating sheet or other support, as will be hereinafter described.
• a layer of the active material of the finished elements with suitable circulating channels. and to prevent the active material from being applied to the edge portions of the insulating sheets or supports.
• means are provided for blocking out certain portions of the said sheets or supports. this means as shown consisting of the flanges 8 already referred to. and a member 10 which is preferably in the form of a rectangular bar and which is suitably secured as by means of screws 11, to the bottom of the channel 4 of the base.
• the bar 10 extends entirely across the opening A and it is important that said bar be secured to the base 1 so that it will be midway between the opposite side walls of the section 7 of such opening.
• the base 1 is provided wit centering ins 12 which respectively engag openings ormed in the bar '10 adjacent/the ends thereof as shown.
• the lower surfaces of the end portions of bar 10 closely engage the bottom of the channel 4, while the intermediate portion of said bar is formed to extend downwardly within the section 7 of the opening A with the lower surface thereof flush with the lower surfaces of the flanges 8.
• That portion of the bar 10 which extends within the section 7 of the opening A is provided adjacent its ends with enlarged circular portions 13 the lower surfaces of which are flush with the lower surfaces of the flanges 8, and midway between its ends with another similar but smaller circular portion 14.
• the hopper device 2 comprises two members 15 and 16 having spaced opposed oppositely inclined walls between which the hopper 3 is formed, said members being seoured between two side plates 17 and 18 by means of screws 19 an rivets 20.
• the members 15 and 16 of the hopper device 2 are a little less in width than the channel 4 of the base 1, and the hopper device is re movably positioned on the base with the lower portions of the members 15 and 16 disposed in the channel 4 and with shoulders 17 and 18' formed adjacent the lower edges of the side plates 17 and 18 resting upon the tracks provided by theupper surfaces of the sides of the channel.
• the parts of the hopper device are so constructed and arranged that when the device is thus positioned, the lower edge of member 15 will lie closely adjacent the upper surface of the bar 10 and there will be a slight clearance between the lower surface of that portion of the hopper member 16 adjacent the discharge opening of the hopper and the bottom of the channel 4 and the upper surfaces of the enlarged circular portions 13 and 14 of bar 10.
• the reduced portions of the side plates 17 and 18 below the shoulders 17 and 18' are of such thickness that when the hopper device 2 is in the position described, they will lie very close to the adjacent side walls of the channel 4.
• the bottom edges of the side plates 17 and 18 for the major portion of the length of said plates, are flush with the bottom of the hopper member 16.
• the hopper member 16 is provided on its under side and centrally thereof with a longitudinally extending rectangular recess 28 and the plate 22 is provided with a similar recess 29 aligned with the recess 28, said recesses being engag i by the bar 10 when the hopper device 2 is positioned on the base 1.
• FIGs. 3 and 4 I have shown an improved electrode element in accordance with my invention and consisting of an asbestos or other insulating sheet 30 having on one side a thin layer of iron-containing material, such as iron or oxide of iron, and on the other side a thin layer of nickel hydroxide. Adjacent its ends and midway between its side edges the asbestos sheet 30 is provided with circular openings 33 through which the poles of the battery pile extend when a plurality of the electrode elements are assembled into a battery pile, as described above.
• the sheet 30 is also provided with a smaller central circular opening 34, and when a plurality of elements such as described are assembled into a battery pile, the central openings thereof provide a path for the circulation of electrolyte.
• each surface of the insulating sheet is provided with uncovered portions carrying no active material, namely, the edge portions 8, the annular portions 13 and 14. surrounding the openings 33 and 34, and the straight narrow portions orchannels 10 located midway of the edges of the sheet and extending between the annular portions 13' and 14' and from the annular portions 13' to the ends of the layer of active material.
• the corresponding channels in the layers of active material as well as the other corresponding uncovered portions of the opppsite surfaces of the insulating sheet will in alignment.
• the asbestos sheet 30' thereof has a channeled layer of active material 35 applied to but one side thereof.
• the hopper device 2 is then positioned on the base 1 with the discharge opening of the hopper over the bottom of the channel 4 of the base at the right of opening A, and the hopper is filled with the dry, loose, finely divided active material to be deposited, for example, finely divided iron or oxide of iron.
• the hopper 3 is of such size as to hold a quantity of active material somewhat in excess of that necessary to form one complete layer of active material of the desired thickness.
• the hopper device 2 is now moved from right to left on the base 1 (referring to Figs. 1 and 2), so that the discharge opening of the hopper moves entirely across the openings A and 9.
• a layer 31 of finely divided iron is deposited on the upper surface of the prewer plate P, such layer being of a uniform thickness equal to the thickness of flanges 8 and the enlarged circular portions 13 and 14 of bar 10 and covering all surface portions of the presser plate P except those which are blocked out by said flanges 8, member 10 and enlarged portions 13 and 14.
• the edge of the lower beveled end portion 26 of the plate 22 acts as a scraper or evener, whereby the layer 31 of active material produced will be of uniform thickness and W111 have a flat, even upper surface.
• the extensions 20 of the plates 18 and 19 act to define the edges of the layer and to prevent material being displaced latorally beyond the limits defined thereby under the action of the scraper provided by the plate 22.
• the surplus active material in the hopper 3, that is, the material in excess of that sufficient to form the layer 31 is discharged from the hopper through the opening 9.
• the presser plate P with the layer of active material 31 thereon is now removed from the base 1 and a sheet 30 of asbestos or other suitable insulating material is placed on the layer 31.
• the presser plate P is then again disposed in the lower section 6 of the opening A with the edge portions of the upper surface of the asbestos sheet. 30 in engagement with the lower surfaces of the flanges 8.
• a layer 32 of dry, loose, finely di vided nickel hydroxide is now deposited on the upper surface of the asbestos sheet 30 lllU in the same manner as the layer of iron or oxide of iron was deposited on the presser late P.
• the presser plate P carrying the a-yers of active material 31 and 32 and the intermediate asbestos shoe- ? 3O is now removed from the base 1, asecond presser plate similar to plate P is placed on the upper layer 32 of active material, and this assembly is then subjected to an enormous pressure, preferably a pressure of several tons per square inch, in a hydraulic press. Under this pressure the layers 31 and 32 of dry, loose, finely divided active material are compacted and formed into dense coherent channeled sheets of uniform thickness with smooth fiat surfaces and are firmly united to the respective surfaces of the asbestos sheet 30.
• the layers of active material on the two asbestos sheets thus united should of course be respectively formed of nickel hydroxide and iron or oxide of iron.
• the method which consists in applying a layer of finely divided active material in a dry, loose state to the surface of a support of fibrous insulating material and then subjecting the support with the layer of active material thereon to a pressure sufficient to compress the active material into a dense coherent sheet and firmly unite the same to said support, substantially as described.
• the method which consists in applying a layer of finely divided active material in a dry, loose state to the surface of a support of fibrous insulating material and then subjecting the said support with the layer of active material thereon to a pressure of from 2 to 10 tons per square inch, substantially as described.
• the method which consists in applying to an insulating sup ort a layer consisting of a mass of finely ivided active material and providing such layer with channeling extending therethrough adapted to expose portions of the surfaces of said support and of the conducting element to be disposed adjacent said layer, and then subjecting such support with the active material applied thereto, to a pressure sufiicient to compress the active material into a dense, coherent, channeled layer and firml unite the'sarne with said support, substantially as described.
• the method which consists in depositing on an insulating support a layer of finely divided active material and partly blockingout such support during the deposition of said material thereon so that said layer will be provided with channeling extending therethrou h and adapted to expose portions of the sur aces of said support and of the conducting element to be disposed adjacent said layer, and then subjecting said support with the active material applied thereto to a pressure suificient to compress the active material into a dense coherent channeled layer and firmly unite the same with said support, substantially as described.
• An element for storage battery cells comprising an insulating sheet having a layer of finely divided nickel hydroxide applied to one surface thereof and a layer of finely divided electrolytically active iron applied to the opposite surface thereof, each of said layers comprisin separated sections having channeling there etween, the material of said sections bein compacted into dense coherent masses, t e corresponding sections of the layers on the opposite surfaces of said sheet being aligned and the channelings in each of said layers being adapted to expose portions of t e surfaces of said sheet and of the conducting element.
• An electrode element for storage battery cells comprising an insulating member
• each of said layers of active material having channeling therethrough adapted to expose portions of the surfaces of said insulating member and of the conducting member to be disposed adjacent such' layer, the cliannelings of the two layers of active material being aligned so that corres onding portions of the opposite surfaces 0 said member are uncovered.
• An electrode element for storage battery cells comprisin a support having an opening therethrougli for the passage of electrolyte and a layer of active material applied to said support, said layer of active material having channeling therethrough communicating with said opening, substantially as described.
• An electrode element for storage ba'ttery cells comprising a support having an opening therethrough for the passage of electrolyte and la ers of active material respectively applie to the opposite surfaces of said support, each of said layers of active material having channeling therethrough communicating with said opening, substan tially as described.

Landscapes

• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Electrochemistry (AREA)
• General Chemical & Material Sciences (AREA)
• Battery Electrode And Active Subsutance (AREA)

Description

Priority Applications (2)

Applications Claiming Priority (1)

Publications (1)

Family

ID=21939845

Family Applications (1)

Country Status (1)

Cited By (9)

• 1925
  • 2025-08-04 US US45781A patent/US1649579A/en not_active Expired - Lifetime

Similar Documents